Damage Evolution Characterization of Low Carbon Alloy Steel Based on Multiaxial Fatigue Test and DIC

Abstract: Fatigue damage and subsequent failure account for the majority of crane structural failure. In this paper, the fatigue damage evolution behavior of low carbon alloy steel Q355B under ...
IEEE

Report on Over 25 000 Cycles Fatigue Test Results of a REBCO HTS Coil and Crossover Joint in a 7 T Background Magnetic Field at 4.2 K

Abstract: This study presents experimental results on the fatigue characteristics of a REBCO coil and crossover joint, aiming to determine whether they can withstand cyclic loading up to the condition ...